Effect of Recycled Polyvinyl Butyral (rPVB) Addition on the Tribological Performance of Glass–Fiber Reinforced Polyamide (PAGF) during Reciprocating Sliding Wear Conditions
Plastic recycling in the automotive industry is a priority. In this study, the effect of adding recycled polyvinyl butyral (rPVB) from automotive windshields on the coefficient of friction (CoF) and specific wear rate (k) of a glass–fiber reinforced polyamide (PAGF) is investigated. It was found that, at 15 and 20 wt.% of rPVB, it acts as a solid lubricant, reducing CoF and k up to 27% and 70%, respectively. Microscopical analysis of the wear tracks showed that rPVB spreads over the worn tracks, forming a lubricant layer, which protects the fibers from damage. However, at lower rPVB content, fiber damage cannot be prevented as the protective lubricant layer is not formed.
Publication date: 05/06/2023
Author: Isabel Ariadna Carmona-Cervantes
Reference: doi: 10.3390/polym15112580
This project has been co-funded with the support of the LIFE financial instrument of the European Union [LIFE17 ENV/ES/000438] Life programme
The website reflects only the author's view. The Commission is not responsible for any use thay may be made of the information it contains.Last update: 2022-01-31