Technology provides sustainable approach to reusing valuable thermoplastic scrap in chips-based laminate.

Process for resuing thermoplastic tape scrap

Van Wees UD and Crossply Technology BV has developed a high-speed process technology that enables converters and part manufacturers to reuse thermoplastic tape and thermoset scrap to produce chip-based laminates that still offer half the flexural strength and modulus of continuous-fiber tapes in the same material/fiber
configuration.

Source | Van Wees UD and Crossply Technology BV



From scrap to chips

During die-cutting operations to produce net-shape preforms from tailored-fiber laminates in thermoplastic UD tapes prior to molding, scrap is collected and segregated by resin and fiber type. That irregularly shaped and sized scrap is then further chopped to produce chips with a maximum size of 50 by 50 millimeters. 

Source | Van Wees UD and Crossply Technology BV



Consolidated sheet

The chips are pressed into a consolidated sheet via compression or vacuum molding. No additional resin is required to make the laminate, which features randomly oriented, discontinuous reinforcements that provide good and orthotropic properties. The chips-based laminate can then be cut and either compression molded or injection overmolded.

Source | Van Wees UD and Crossply Technology BV



No signs of performance loss

A study conducted by Van Wees compared the properties of UD tailored-fiber laminates (second from top) in several resin and fiber configurations as well as chips-based laminates (top) from scrap produced creating preforms from the UD tailored-fiber laminates vs. a fabric-reinforced organosheet to produce door crash beams (B-side of molded part third from top and A-side of part, bottom). The researchers saw little difference in performance between the part in continuous/UD-fiber laminates vs.
a hybrid of the chips laminate in the core and continuous/UD-fiber laminates in the skins.

Source | Van Wees UD and Crossply Technology BV



High-speed process

The zero-waste process is designed to operate at high production speeds to match other company equipment. For the door crash beam, researchers estimated that with just one multiaxial UD machine (capable of producing 1,800 preforms/hour), the system could easily meet project goals of 2 million parts/year. By adding the additional equipment to convert scrap to chips-based laminates, production volumes would increase 30 percent to 2.6 million parts/year with no waste. 

Source | Van Wees UD and Crossply Technology BV



Previous Next $(document).ready(function () { //$('.carousel-item').first().addClass('active'); //$('.carousel-indicators > li').first().addClass('active'); $('').swiperight(function () { $(this).carousel('prev'); }); $('').swipeleft(function () { $(this).carousel('next'); }); $('').carousel({ pause: true, interval: false }); }); One challenge to kitting prepreg fabrics or unidirectional (UD) tapes is figuring out what to do with trimmings that are too small or whose fibers are incorrectly aligned for reuse in another project. Although nesting software and cutters have reduced scrap significantly, trimmings still often go into a landfill, which adds to material and part costs as well as environmental burden. However, a Dutch company, Van Wees UD and Crossply Technology BV (Tilburg, Netherlands), is helping improve sustainability by developing a new technology — and the machines that make it possible — to reuse thermoplastic tape offal.

Textile rootsFounded in 1945 and with deep roots in the textile industry, Van Wees is a full-service provider that designs, produces, installs and commissions machines and production lines to produce advanced composites (thermoset or thermoplastic, carbon or glass fiber) with a focus on high-quality, high-volume production methods. The company makes prepreg impregnation lines (including creels) — primarily for epoxies on the thermoset side and for materials ranging from polypropylene (PP) to high-temperature polyamides (PAs) on the thermoplastic side — as well as crossply and multiaxial UD tape placement machines, which can process either thermoplastic or thermoset tapes. A sister company, Eltra Engineering BV (also in Tilburg) specializes in industrial automation technology and supplies electrical controls and software for Van Wees machines.

Related Stories _jwl(function() {ga('send', 'pageview', { 'page' : '/virtual/Ad/Native - CW Prepreg Zone/Impression/Henkel AG 46 Co. KGaA (henkelag) Button 2 - Standard id:10283'});}); _jwl(function() {ga('send', 'pageview', { 'page' : '/virtual/Ad/Native - CW Prepreg Zone/Impression/Gardner Business Media Inc. (gardpub) Button 1 - Standard id:10282'});}); _jwl(function() {ga('send', 'pageview', { 'page' : '/virtual/Ad/Native - CW Prepreg Zone/Impression/IMTS - International Manufacturing Technology Show (imts) Button 1 - Standard id:10510'});}); _jwl(function() { document.addEventListener('DOMContentLoaded', function() { // Ensure the "Related Stories" isn't nested in anything that'd cause an odd render var promo = document.querySelector('.blogPost .DisplayBar.promo-horizontal, #articleBody .DisplayBar.promo-horizontal'); if (promo !== null) { var promoParent = promo.parentElement; if (promoParent.id !== 'short' && promoParent.id !== 'articleBody') { promoParent.parentElement.insertBefore(promo, promoParent.nextElementSibling); } } })});At its Research and Technology Center (R&TC), Van Wees maintains production-scale equipment for its own process development as well as for customers considering a Van Wees system, or who are learning to operate equipment while waiting for their machines to be built. This allows customers to produce material that they can evaluate or, in turn, offer to their own customers for evaluation. For example, at the R&TC, tows can be pulled from a creel and fibers spread and impregnated to produce tapes, which then can be fed through the company’s crossply or multiaxial UD machines to produce laminates with a variety of ply layers and fiber orientations. (Crossply laminates have at least two plies oriented at 0/90 degrees and multiaxial UD laminates have at least two UD plies oriented at angles other than 0/90 degrees.) Laminates exiting these machines are tacked together for ease of handling. They may next be die-cut into net-shape preforms that are then ready for processing into a composite part. Although Van Wees’ equipment focus with the crossply and multiaxial UD equipment is on production of UD thermoplastic tapes, the machines can be used to produce tapes with  thermoset matrices and/or with fabric rather than UD reinforcements.

Interestingly, it was Van Wees’ own scrap problem from making these products for customer testing, as well as customer requests, that led company researchers to develop a “zero-waste process” to recycle chips/offal from preform production using tailored-fiber blanks. As a service, the company is offering customers the opportunity to evaluate these chip-based thermoplastic blanks and already has developed equipment to commercially produce them at high production volumes.



Waste not, want notDuring die-cutting operations to make net-shaped preforms (which Van Wees calls “patches”), scrap material is collected and segregated by resin and fiber type. This scrap is irregularly shaped and sized, so die cutters are designed to produce “chips” with a maximum size of 50 by 50 millimeters. Chopped chips are then pressed into a consolidated sheet (via compression or vacuum molding), resulting in a laminate with randomly oriented, discontinuous fibers. No additional resin is needed to make the sheet, and only chips with chemically compatible resins are mixed together, although both glass and carbon fiber-reinforced chips may be combined depending on properties desired in the final part that will be formed from the chips-based laminate.

Because fibers in individual chips within the laminate can be up to 50 millimeters long, and fiber orientation across the sheet is random, the 100 percent recycled, zero-waste tailored blanks provide good and orthotropic stiffness and strength — particularly compared with short-fiber injection molding compounds. However, since fiber weight fractions for the laminates’ discontinuous fiber bundles can run 50-70 percent — with initial formulations on the high end of that range — the material can barely flow in a compression press. Therefore, to fill 2.5D or 3D geometry, the chip-based laminate must be overmolded with short fiber or even neat resin in an injection molding machine. It also could be co-molded with a continuous-fiber material in a compression press. Either way, the laminate does need to be preheated prior to molding.

Interestingly, Van Wees has found that the chip-based panels still provide half the bending strength and modulus of its high-performance, continuous-fiber crossply panels in the same fiber and resin configuration.

Concept prove outTo showcase the capabilities of its zero-waste tailored blanks, Van Wees has conducted several demonstrator projects. One was a stiffening/crash beam for door inner panels on a passenger car. This effort was based on the Lipa Series project, which developed lightweight composite parts for series production for a range of industries. The now-inactive consortium based in Büsslingen, Switzerland, built on core technologies involving preforming continuous-fiber organosheet/glass-mat thermoplastic (GMT) composites and then back filling with fiber-reinforced resin in an injection molding machine.

Van Wees’ demonstrator beam (a part used to pass side impact/intrusion regulations) was approximately 650 millimeters long, 110 millimeters wide, had a nominal wall of 3 millimeters, and weighed roughly 450 grams in the benchmark material, which was a 3-millimeter glass fabric-reinforced PA6. The part also featured a domed structure in the center that was 40 millimeters high. The organosheet crash beam did not provide sufficient energy absorption to meet application requirements, so Van Wees researchers attempted to improve overall performance in the same wall thickness (since existing tooling was used), in a cycle time of less than one minute and with zero waste.

Working with several polymer suppliers, Van Wees produced UD tapes in-house using several polymers and reinforcements — including glass fiber/PA4/10, glass fiber/PP, carbon fiber/PP, and glass + carbon fiber/PP. Matching short-fiber injection overmolding compounds were produced by the resin suppliers. Simulation was used to evaluate the number and orientation of individual UD plies for tailored blanks in order to meet or exceed performance requirements. Next, tapes were used to produce continuous-fiber laminates, from which the crash beams were produced. Computer-aided engineering (CAE) results predicted the glass fiber/PA4/10 tailored blanks would provide the best properties at lower cost than the fabric/organosheet, and physical testing confirmed this.

To further explore opportunities to reduce waste and cost, researchers reused scrap (approximately 30 percent cutting losses) generated from producing continuous fiber laminates to produce crash beams, recycled that material into chip-based laminates that were 1-millimeter thick, and used that product as a core layer (replacing three UD plies) between “skins” of more UD material made on the multiaxial UD machine. Interestingly, in preliminary tests with a limited sample size, they saw little or no loss in performance for the hybrid laminates with a mix of continuous and discontinuous reinforcement compared to the full continuously reinforced laminates.

Additional calculations conducted by the team indicated that it would be possible to meet Van Wees’ production goals of 2 million crash beams per year, using the 1-minute composite overmolding process developed by the Lipa Series team. Given the speed at which the Van Wees tailored-blank production lines operate (1,800 patches/hour on the multiaxial UD machine and 1,260 patches/hour on the crossply machine), adding additional equipment to convert scrap into chips-based laminates would create a zero-waste production system and increase production volumes 30 percent to 2.6 million parts per year. Ironically, the injection molding machines would be the rate-limiting step in this production sequence — something that doesn’t often happen.

Another rapid-turnaround project that company researchers conducted was to develop composite-faced door handles for the conference room at Van Wees headquarters. Final composite inserts were available for attendees to view at last year’s Composites Overmolding conference.

“Co-development and innovation are the driving forces of modern industry,” notes Rien van den Aker, Van Wees director. “We believe that joint development with all the players in the composite chain is of prime interest. Metals are the competitors of our industry and are made in the most rational way. Therefore, it will only be with intelligent processes and equipment that we can introduce lightweight composite products into high-volume applications.” He emphasizes that it will take a joint effort among supply chain members to make zero-waste production of thermoset and thermoplastic composite parts possible. “Van Wees is happy to assist interested parties with product and process development,” he adds.